Formulation ceramic mass for porous coating, using tropical wood wastes
DOI:
https://doi.org/10.5902/1980509870383Keywords:
Tropical wood wastes, Ceramic materials, Technological properties, Sustainable alternativeAbstract
The powder wastes of tropical wood Angelim Rajado (AR) (Pithecelobium racemosum Ducke) and Sucupira Vermelha (SV) (Andira parviflora Ducke), generated in the wood industry in Itacoatiara – Amazonas state, Brazil are usually deposited in inappropriate places. In this work, clay was partially replaced by wastes in the manufacture of ceramic materials to development of a new material for application in porous wall covering (tile) (BIII type), as a sustainable alternative for the Ceramic Pole of the municipality of Iranduba – AM. Specimens (60mm x 20mm x 8mm) were formed by uniaxial pressing (20 MPa) dried at 110ºC per 24h and fired at 750 and 850ºC. The effects of the sintering process on ceramic masses with SV and AR wood wastes were studied by TGA-DSC, XRF (X-Ray Fluorescence) and XRD (X-Ray Diffractometer). After firing, the samples were subjected to the following technological characterizations: water absorption, linear retraction, apparent density, apparent porosity, and modulus of rupture at flexure. The mineralogical and microstructural characteristics were also analyzed. The results show that up to 10% of AR and SV wood wastes in powder form can be incorporated into structural ceramic masses for the production of ceramic materials. However, formulations with 5 and 10% of the SV waste present superior results at the same proportions with AR, being in agreement with the parameters of NBR 13818 (Brazilian Technical Regulation Association).
Downloads
References
ABJAGHOU, H. et al. Incorporation of Wooden Furniture Wastes in Fired Clay Bricks for Improved Thermal Insulation: A Feasibility Study. Waste and biomass valorization, [S.l.], v. 11, n. 12, p. 6943-6951, Jan. 2020. DOI https://doi.org/10.1007/s12649-020-00933-6.
ALMEIDA, E. P. et al. Preparação de blocos porosos utilizando resíduos de MDF na formulação de massas cerâmicas estruturais. Revista Matéria, [S.l.], v. 25, n. 1, 2020. DOI https://doi.org/10.1590/S1517-707620200001.0918.
ARTHUR, E. K.; GIKUNOO, E.; ZALNEZHAD, E. (Rev. ed.). Property analysis of thermal insulating materials made from Ghanaian anthill clay deposits. Cogent Engineering, [S.l.], v. 7, n. 1, Oct. 2020. DOI https://doi.org/10.1080/23311916.2020.1827493.
ASSOCIAÇÃO BRASILEIRA DE NORMAS TÉCNICAS. NBR 13818: Placas Cerâmicas para Revestimento: Especificação e Métodos de ensaio. Rio de Janeiro, 1997. 78p.
ASSOCIAÇÃO BRASILEIRA DE NORMAS TÉCNICAS. NBR 6459: Solo: determinação do limite de liquidez. Rio de Janeiro, 1984a. 3 p.
ASSOCIAÇÃO BRASILEIRA DE NORMAS TÉCNICAS. NBR 6508: Grãos de solos que passam na peneira de 4,8 mm: Determinação da massa específica. Rio de Janeiro, 1984b.
ASSOCIAÇÃO BRASILEIRA DE NORMAS TÉCNICAS. NBR 7180: Solo: determinação do limite de plasticidade. Rio de Janeiro, 1984c. 1 p.
ASSOCIAÇÃO BRASILEIRA DE NORMAS TÉCNICAS. NBR 7181: Solo: análise granulométrica. Rio de Janeiro, 1984d. 13 p.
BORIES, C. et al. Fired clay bricks using agricultural biomass wastes: Study and characterization. Constr. Build. Mater., [S.l.], v. 91, p. 158-163, Aug. 2015. DOI https://doi.org/10.1016/j.conbuildmat.2015.05.006.
CABETE, N. P. F.; CABETE, M. da S.; DACOL, S. Manejo florestal sustentável: o caso da Mil Madeiras Preciosas. XXIX ENCONTRO NACIONAL DE ENGENHARIA DE PRODUÇÃO (ENEGEP), 29., 6-9 out. 2009, Salvador, BA. Anais [...]. Rio de Janeiro: ABEPRO, 2009. Tema: Engenharia de Produção e o Desenvolvimento Sustentável: Integrando Tecnologia e Gestão.
CONTRERAS, M. et al. Recycling of industrial wastes for value-added applications in clay-based ceramic products: a global review (2015–19), New Materials in Civil Engineering, Butterworth-Heinemann [Ed.], Oxford, p. 155-219, 2020. DOI https://doi.org/10.1016/B978-0-12-818961-0.00005-3.
COUTINHO JR, T. A.; CARVALHO, S. G.; ZANARDO, A. Características Mineralógicas e Químicas do Minério da Mina Morro Alto: Possibilidades de Fabricação de Revestimento Cerâmico Monoporoso por Via Seca. Cerâmica Industrial, [S.l.], v. 18, n. 5-6, 2013. Disponível em: https://www.ceramicaindustrial.org.br/article/587657537f8c9d6e028b47f0. Acesso em: 5 maio 2022.
DUTRA, L. F. et al. Microstructural characterization of porous clay-based ceramic composites. Materials, [S.l.], v. 12, n. 6, Mar. 2019. DOI 10.3390/ma12060946.
GENG, J.; SUN, Q. Effects of high temperature treatment on physical-thermal properties of clay. Thermochimica Acta, [S.l.], v. 666, p. 148–155, 2018. DOI https://doi.org/10.1016/j.tca.2018.06.018.
GUZMAN, Ya. Certain Principles of Formation of Porous Ceramic Structures. Properties and Applications (A Review). Glass & Ceramics, [S.l.], v. 60, p. 280-283, Sept. 2003. DOI https://doi.org/10.1023/B:GLAC.0000008227.85944.64.
HOSSAIN, Sk. S.; ROY, P. K. Sustainable ceramics derived from solid wastes: a review. Journal of Asian Ceramic Societies, [S.l.], v. 8, n. 4, p. 984-1009, Sept. 2020. DOI https://doi.org/10.1080/21870764.2020.1815348.
KAZA, S. et al. What a Waste 2.0: A Global Snapshot of Solid Waste Management to 2050. Washington, DC: World Bank Group, 2018. Disponível em: https://openknowledge.worldbank.org/handle/10986/30317. Acesso em: 5 maio 2022.
MAGLIANO, M. V. M., PANDOLFELLI, V. C. Mulitização em refratários utilizando diferentes fontes precursoras: revisão. Cerâmica, [S.l.], v. 56, n. 340, p. 368-375, 2010. DOI https://doi.org/10.1590/S0366-69132010000400009.
MAHMOUDI, S.; SRASRA, E.; ZARGOUNI, F. The Use of Tunisian Barremian Clay in the Traditional Ceramic Industry: Optimization of Ceramic Properties. Applied Clay Science, [S.l.], v. 42, n. 1-2, p. 125-129, Dec. 2008. DOI http://dx.doi.org/10.1016/j.clay.2007.12.008.
MORI, F. A.; COVEZZI, M. M.; MORI, C. L. S. O. Utilização da Serragem de Eucalyptus Spp. para a produção de tijolo maciço cerâmico. Floresta, Curitiba, PR, v. 41, n. 3, p. 641-654, jul.-set. 2011. DOI http://dx.doi.org/10.5380/rf.v41i3.24057.
OKADA, K. et al. Porous ceramics mimicking nature: preparation and properties of microstructures with unidirectionally oriented pores. Science and Technology of Advanced Materials, [S.l.], v. 12, n. 6, Oct. 2011. DOI https://doi.org/10.1088/1468-6996/12/6/064701.
PERALTA-SÁNCHEZ, M. G. et al. Viabilidade do uso de argilas cauliníticas do Quadrilátero Ferrífero para a indústria cerâmica. Ceramica, [S.l.], v. 57, n. 343, set. 2011. DOI https://doi.org/10.1590/S0366-69132011000300002.
RODRIGUES, M. I. B. et al. Sustainable Development for residues generated in the Red Ceramic industries region in the region of Cariri – CE. Brazilian Journal of Development, Curitiba, v. 7, n. 4, p. 40689-40702, Apr. 2021. DOI https://doi.org/10.34117/bjdv7n4-500.
RODRIGUES, V. O. et al. Caracterização das Matérias Primas Empregadas na Fabricação de Produtos do Pólo Cerâmico de Iranduba-AM. Cerâmica Industrial, Criciúma – SC, v. 20, n. 1, p. 37-40, jan.-fev. 2015. DOI http://dx.doi.org/10.4322/cerind.2015.002. Disponível em: https://ceramicaindustrial.org.br/article/5876575a7f8c9d6e028b4819. Acesso em: 5 maio 2022.
ROQUE, R. A. L.; PIERRI, A. C. Uso inteligente dos recursos naturais e sustentabilidade na construção civil. Pesquisa, Sociedade e Desenvolvimento, Itabira-MG/Vargem Grande Paulista-SP, v. 8, n. 2, pág. e3482703, 2019. DOI https://doi.org/10.33448/rsd-v8i2.703. Disponível em: https://rsdjournal.org/index.php/rsd/article/view/703. Acesso em: 3 abr. 2022.
SANTOS, C. P. et al. Caracterização de argilas calcárias utilizadas na produção de revestimentos cerâmicos no Estado de Sergipe – Brasil. Cerâmica, [S.l.], v. 62, n. 362, abr.-jun. 2016. DOI https://doi.org/10.1590/0366-69132016623621983.
SERAFINI, R.; CARVALHO, J. P. B.; FIGUEIREDO, A. D. de. Impactos ambientais e toxicológicos da lixiviação em tijolos cerâmicos com adição de resíduos: uma revisão bibliográfica. Revista Técnico-Científica do Crea-PR, Ed. Especial 3° Simpósio Paranaense de Patologia das Constuções (SPPC), Curitiba, 17 p., ago. 2018. Disponível em: https://revistatecie.crea-pr.org.br/index.php/revista/article/view/416. Acesso em: 5 maio 2022.
SILVA, A. L. da et al. Technological characterization of new clay deposits in the south region of Amapá aiming applications in the ceramic industry. Matéria, Rio de Janeiro, v. 22, n. 1, 2017. DOI https://doi.org/10.1590/S1517-707620170001.0129.
SLIMANOU, H. et al. Thermal, physical, mechanical and microstructural properties of dredged sediment-based ceramic tiles as substituent of kaolin. Environmental Science and Pollution Research, [S.l.], v. 29, p. 26792–26809, 2022. DOI https://doi.org/10.1007/s11356-021-16787-x.
SOUZA, J. A. et al. Resíduos da Construção Civil: estudo comparativo de duas empresas de Rondonópolis-MT. Revista Estudos e Pesquisas em Administração, Rondonópolis, v. 3, n. 2, p. 53-67, 2019. DOI 10.30781/repad.v3i2.8549. Disponível em: https://periodicoscientificos.ufmt.br/ojs/index.php/repad/article/view/8549. Acesso em: 5 maio. 2022.
VANUZA O. S. et al. Pyrolysis of acai seed biomass: Kinetics and thermodynamic parameters using thermogravimetric analysis, Bioresource Technology Reports, Volume 12, 2020, 100553. https://dx.doi.org/10.1016/j.biteb.2020.100553
VELASCO, P. M. et al. Development of sustainable fired clay bricks by adding kindling from vine shoots: Study of thermal and mechanical properties. Applied Clay Science, [S.l.], v. 107, p. 156-164, Apr. 2015. DOI https://doi.org/10.1016/j.clay.2015.01.017.
ZANELLI, C. et al. Technological behavior of porcelain stoneware bodies with Egyptian syenites. Applied Ceramic Technology, [S.l.], v. 16, n. 2, p. 574-584, Mar.-Apr. 2019. DOI https://doi.org/10.1111/ijac.13102.
ZHANG, Z. et al. Geopolymer foam concrete: An emerging material for sustainable construction. Construction and Building Materials, [S.l.], v. 56, p. 113-127, Apr. 2014. DOI 10.1016/j.conbuildmat.2014.01.081.
Published
How to Cite
Issue
Section
License
Copyright (c) 2022 Ciência Florestal
This work is licensed under a Creative Commons Attribution-NonCommercial 4.0 International License.
A revista CIÊNCIA FLORESTAL reserva-se o direito de realizar, nos originais, alterações de ordens normativas, ortográficas e gramaticais, com vistas a manter o padrão escolar da língua, mas respeitando o estilo dos autores. As provas finais podem ou não ser enviadas aos autores.