Production and evaluation of particleboard made of sawdust and sugarcane bagasse with polyurethane resin based on castor oil
DOI:
https://doi.org/10.5902/2236117038531Keywords:
Particleboards, Wood waste, Agroindustrial wasteAbstract
Among the goals for sustainable development in Brazil, studies have been conducted to better use of industrial and agricultural waste to promote adequate final disposal of these and generate new materials that minimize the exploitation and use of natural resources. In this work, the proposal is to make and evaluate boards with nominal density of 0.80 g.cm-3 using sugar cane bagasse, sawdust and polyurethane resin derived from castor oil. Thus, three treatments with different percentages of particles and 10% of PU-castor were proposed for the preparation of boards that were pressed with a pressure of 50 kgf.cm-2, a temperature of 100°C and a pressing time of ten minutes. The boards were evaluated for their physical properties (density, moisture content and swelling) and mechanical (static flexure and perpendicular traction) according to NBR 14810: 2-2013 and presented average values density of 936 to 937 kg.m-3, swelling after 24 hours of 5.0 to 7.2%, modulus of resistance to static bending of 22 to 23 MPa and perpendicular traction of 0.71 to 0.87 MPa. The results obtained with the tests indicate the great potential of use of sugarcane bagasse and sawdust to produce boards of high density particles.
Downloads
References
ABNT - Associação Brasileira De Normas Técnicas. NBR NM 248: Agregados - Determinação da composição granulométrica. Rio de Janeiro, 2003.
ABNT - Associação Brasileira De Normas Técnicas. NBR 14810-1: Painéis de partículas de média densidade - Parte 1: Terminologia. Rio de Janeiro, 2013.
ABNT - Associação Brasileira De Normas Técnicas. NBR 14810-2: Painéis de partículas de média densidade - Parte 2: Requisitos e Métodos de Ensaio. Rio de Janeiro, 2013.
Araújo, L. C. R. Caracterização química e mecânica de poliuretanas elastométricas baseadas em materiais oleoquímicos. São Carlos, 1992. Dissertação (Mestrado) – Instituto de Física e Química de São Carlos – USP.
Battistelle, R. A. G.; Marcilio, C.; Lahr, F. A. R. Emprego do bagaço da cana-de-açúcar (saccharum officinarum) e das folhas caulinares do bambu da espécie dendrocalamus giganteusna produção de chapas de partículas. Revista Minerva, v. 5, n. 3, p. 297 305, 2009.
Bertolini, M. S. Emprego de resíduos de Pinus sp tratado com preservantes CCB na produção de chapas de partículas homogêneas utilizando resina poliuretana à base de mamona. 2011. 128 f. Dissertação (Mestrado) - Escola de Engenharia de São Carlos, Instituto de Física de São Carlos, Instituto de Química de São Carlos da Universidade de São Paulo, São Carlos, 2011.
Cerqueira, P. H. A. et al. Análise dos resíduos madeireiros gerados pelas serrarias do município de Eunápolis-BA. Floresta e Ambiente, [s.l.], v. 19, n. 4, p.506-510, 2012. FapUNIFESP (SciELO). Available from: http://dx.doi.org/10.4322/floram.2012.051
CMMAD - Comissão Mundial Sobre Meio Ambiente E Desenvolvimento. Relatório Brundtland, 1988, p. 49.
CONAB - Companhia Nacional de Abastecimento. V. 4 - SAFRA 2017/18 N.2 - Segundo levantamento, Agosto 2017.
Contreras, W. M.; Owen, M. E. C.; Cloquell, V. B.; Contreras, Y. M.; Garay, D. A. J. Diseño de tableros de partículas de caña brava y adhesivo fenol – formaldehído. Revista Forestal Latinoamericana, v. 21, n. 39, p. 39- 55, 2006.
Santos, M.F.N., Battistelle, R.A.G., Bezerra, B.S., Varum, H.S.A. Comparative study of the life cycle assessment of particleboards made of residues from sugarcane bagasse (Saccharum spp.) and pine wood shavings (Pinus elliottii). Journal of Cleaner Production, Volume 64, Issue undefined, 1 February 2014.
Fiorelli, J. et al. Painéis de partículas à base de bagaço de cana e resina de mamona – produção e propriedades. Acta Scientiarum Technology, v.33, n.4, p.401-406, 2011.
Iwakiri, S. Painéis de madeira reconstituída. Ed. FUPEF – Fundação de Pesquisas Florestais do Paraná. Curitiba, PR, p.123-166, 2005.
Mandes, R. F. Painéis aglomerados produzidos com bagaço de cana em associação com madeira de eucalipto. Scientia Forestalis, Piracicaba, v. 38, n. 86, p. 285-295, jun. 2010.
Nolasco, A. M. Resíduos florestais. Piracicaba: ESALQ/ USP, Departamento de Ciências Florestais, 1998.
Okino, E. Y. A.; Andahur, J. P. V.; Santana, M. A. E.; Souza, M. R. Physico-mechanical properties of chemically modified sugar cane bragasse partideboards. Scientia Forestalis, v. 1, n. 52, p. 35-42, 1997.
Saravia-Cortez, A.M.; Herva, M., García-Diéguez, C.: Roca, E.. Assessing environmental sustainability of particleboard production process by ecological footprint. Journal of Cleaner Production 52 (2013) 301 e 308.
Silva, V. L. M. M.; GOMES, W. C. O.; ALSINA, L. S. Utilização do bagaço de cana de açúcar como biomassa adsorvente na adsorção de poluentes orgânicos. Revista Eletrônica de Materiais e Processos 2007; 2:27-32, 2007.
Silva, A. J. P.; França Santos, W. L.; Rocco Lahr, F. A. Partículas longas e orientadas de bagaço de cana-de-açúcar na produção de painel similar ao OSB. In. ENCONTRO BRASILEIRO EM MADEIRA E ESTRUTURAS DE MADEIRA, 11., 2008, Londrina. Anais... Londrina: UEL, IBRAMEM, 2008.
Silva, S. A. M. Confecção e avaliação de painéis de partículas de madeira de média densidade com aproveitamento de resíduos industriais. 2016. 92 f. Tese (Doutorado) - Curso de Engenharia Civil, Unesp, Ilha Solteira, 2016. Cap. 1.
TOMASELLI, I. Tendências de mudanças na indústria de painéis. Revista da madeira. P. 36 – 40. 2000.
Torquato, L. P. Caracterização dos painéis MDF comerciais produzidos no Brasil. 2008. 94 f. Dissertação (Mestrado) - Curso de Engenharia Florestal, Universidade Federal do Paraná - UFPR, Curitiba, 2008.
Widyorini, R.; Xu, J.; Umemura, K.; Kawai, S. Manufacture and properties of binderless particleboard from bagasse: effects of raw material type, storange methods and manufacturing process. Journal of Wood Science, v. 51, n. 6, p. 648-654, 2005.
Zau, M. D. L. et al. Avaliação das propriedades química, física e mecânica de painéis aglomerados produzidos com resíduo de madeira da Amazônia - Cumaru (Dipteryx Odorata) e resina poliuretana à base de óleo de mamona. Polímeros, São Carlos, v. 24, n. 6, p.101-108, dez. 2014.
Published
How to Cite
Issue
Section
License
Copyright (c) 2019 Revista Eletrônica em Gestão, Educação e Tecnologia Ambiental
This work is licensed under a Creative Commons Attribution-NonCommercial-ShareAlike 4.0 International License.
DECLARATION